| About |
|---|
| Fortron MT9320C0 is an unfilled grade used for extrusion applications. It demonstrates excellent chemical resistance and thermal stability as well as a high melt strength. Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9320C0 is in compliance with ISO 10993, USP Class VI and it is included in the Fortron Drug and Device Master Files at the FDA. This grade complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good melt strength,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 85.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 6.0 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 4200 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 140 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 95.0 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 115 | ℃ | ISO 75-2/A |
| Glass transition temperature | 90.0 | ℃ | ISO 11357-2 |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 2.80 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 300 to 310 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Nozzle temperature | 300 to 310 | °C | |
| Processing (melt) temperature | 310 to 320 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Injection pressure | 40.0 to 80.0 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 30.0 to 60.0 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |