| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Bending modulus | |||
| 15 mm/min，6.40 mm | 26000 | MPa | ASTM D790 |
| Tensile modulus | |||
| 3.20 mm，1 mm/min | 22000 | MPa | ASTM D638 |
| tensile strength | |||
| 430 | MPa | ASTM D638 | |
| Rockwell hardness | 103 | ASTM D785 | |
| Tensile strain | |||
| Fracture, 3.20 mm, 50 mm/min | 20 | % | ASTM D638 |
| Yield, 3.20 mm, 50 mm/min | 5 | % | ASTM D638 |
| bending strength | |||
| 15 mm/min，6.40 mm | 720 | MPa | ASTM D790 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Flow Rate | |||
| 220℃，10.0kg | 53 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.4-0.7 | % | ASTM D955 |
| Density | 1.18 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 25 | J/m | ASTM D256 |
| -30℃，3.2mm | 8 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 25 | J/m | ASTM D256 |
| -30℃，6.4mm | 8 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 80 | ℃ | UL 746B |
| Impact mechanical performance | 70 | ℃ | UL 746B |
| No mechanical impact | 80 | ℃ | UL 746B |
| Vicat Softening Temp | |||
| B50 | 84 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 76 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 84 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Processing speed | Nominal value | Unit | Test method |
| Processing temperature | Nominal value | Unit | Test method |
| Processing pressure | Nominal value | Unit | Test method |
| Screw speed | 30-60 | rpm | |
| drying temperature | 70-80 | ℃ | |
| Drying time | 2-4 | hrs | |
| Melting temperature | 200-230 | ℃ | |
| Temperature at the rear of the barrel | 170-190 | ℃ | |
| Temperature in the middle of the barrel | 180-200 | ℃ | |
| Front temperature of material barrel | 190-210 | ℃ | |
| Nozzle temperature | 200-230 | ℃ | |
| Mold temperature | 40-60 | ℃ | |
| Back pressure | 5-10 | bar | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |