| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Flame Characteristics,V-0 |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 220℃，10.0kg | 42 | g/10min | ASTM D1238 |
| Density | |||
| 23℃ | 1.16 | g/cm³ | ASTM D792 |
| Shrinkage rate | 0.4-0.7 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 3.20 mm，50 mm/min | 41 | MPa | ASTM D638 |
| Tensile strain | |||
| 3.20 mm，50 mm/min | 23 | % | ASTM D638 |
| bending strength | |||
| 6.40 mm，15 mm/min | 67.689 | MPa | ASTM D790 |
| Bending modulus | |||
| 6.40 mm，15 mm/min | 2256.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa，6.4 mm | 77 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| A50 | 85 | ℃ | ASTM D1525 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃，6.4mm | 22 | kg.cm/cm | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions (injection molding) | Nominal value | Unit | Test method |
| Processing pressure | Nominal value | Unit | Test method |
| drying temperature | 70 ~ 80 | ℃ | |
| Drying time | 2 ~ 3 | hrs | |
| Temperature at the rear end of the barrel | 175 ~ 185 | ℃ | |
| Temperature at the middle end of the barrel | 180 ~ 190 | ℃ | |
| Front end temperature of material barrel | 190 ~ 200 | ℃ | |
| Nozzle temperature | 185 ~ 190 | ℃ | |
| Resin temperature | 200 ~ 220 | ℃ | |
| Mold temperature | 40 ~ 80 | ℃ | |
| Screw speed | 40 ~ 80 | % | |
| Injection pressure | 80 ~110 | MPa | |
| Maintaining pressure | 30 ~ 50 | MPa | |
| Back pressure | 0.5 ~ 1 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |