| About |
|---|
| Product Description | |
|---|---|
| Supplier | Nan Ya |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Flame Characteristics,Heat Resistance, Good,High impact resistance,Low warping |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| 3 mm | 1.2 – 1.9 | % | ASTM D955 |
| Melt index | 10 | g/10min | ASTM D1238 |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23°C，24hrs | 1.5 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 55 | MPa | ASTM D638 |
| Bending modulus | 1800 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2 mm | 9 | KJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.82 MPa | 55 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 80 | ℃ | |
| Drying time | 4 | hrs | |
| Nozzle temperature | 240~255 | ℃ | |
| Barrel temperature – front section | 240~250 | ℃ | |
| Barrel temperature – middle section | 230~245 | ℃ | |
| Barrel temperature – rear section | 225~235 | ℃ | |
| Mold temperature | 60 | ℃ | |
| Injection pressure | 50~150 | MPa | |
| Screw speed | 100~120 | rpm | |
| Injection speed | 快 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |