| About |
|---|
| Product Description | |
|---|---|
| Supplier | Nan Ya |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | processability,Halogen,Mechanical property,Fatigue resistance,high wear resistance ,Flame Characteristics,High strength |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 | g/cm³ | ASTM D792 |
| Melt index | |||
| 275℃，2.16kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3 mm | 0.3 | % | Internal Method |
| TD：3 mm | 0.7 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 155 | MPa | ASTM D638 |
| elongation | 2.5 | % | ASTM D790 |
| bending strength | 245 | MPa | ASTM D790 |
| Bending modulus | 10500 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 1.2 | KJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 233 | ℃ | ASTM D648 |
| Melting temperature | |||
| DSC | 262 | ℃ | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E15 | ohm·cm | ASTM D257 |
| Insulation strength | 18 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1MHz | 3.2 | ASTM D150 | |
| Dissipation factor | |||
| 1MHz | 0.02 | ASTM D150 | |
| Arc resistance | 70 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| Full color, 1.5mm | V-0 | UL 94 | |
| Relative temperature index | |||
| Electrical performance, full-color, 1.5mm | 65 | ℃ | UL 746B |
| Mechanical impact performance, full-color, 1.5mm | 65 | ℃ | UL 746B |
| Non mechanical impact performance, full-color, 1.5mm | 65 | ℃ | UL 746B |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| drying temperature | 80 | ℃ | |
| Drying time | 4 | hr | |
| First stage temperature | 270 | ℃ | |
| Second stage temperature | 280 | ℃ | |
| Third stage temperature | 285 | ℃ | |
| Nozzle temperature | 290 | ℃ | |
| Mold temperature | 85 – 95 | ℃ | |
| Injection pressure | 45 – 100 | MPa | |
| Injection speed | 高速 | ||
| Screw speed | 180 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |