| About |
|---|
| Product Description | |
|---|---|
| Supplier | WOTE |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| Processing performance | Nominal value | Unit | Test method |
| drying temperature | 110 | ℃ | |
| water content | <0.2 | % | |
| Processing temperature range | 275-305 | ℃ | |
| Dehumidification and drying time | 3 | h | |
| Optimal processing temperature | — | ℃ | |
| Mold temperature | 70-95 | ℃ | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| FLAME CHARACTERISTICS | |||
| thickness 1.6mm | V-0 | Class | UL 94 |
| Hot deformation temperature | 137 | ℃ | 0.45MPa |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| IZOD Notch Impact Strength | |||
| -30℃ | 10 | KJ/m² | ISO 180-1A |
| 23℃ | 45 | KJ/m² | ISO 180-1A |
| Tensile modulus | |||
| 1mm/min | 2260 | MPa | ISO 178 |
| bending strength | |||
| 2mm/min | 90 | MPa | ISO 178 |
| Bending modulus | |||
| 2mm/min | 2250 | MPa | ISO 178 |
| Elongation at break | |||
| 50mm/min | 88 | % | ISO 527 |
| tensile strength | |||
| 50mm/min | 56 | MPa | ISO 527 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |