| About |
|---|
| FRAGOM G LCX/3013 is a flame retardant halogen free polyolefin compound. FRAGOM G LCX/3013 is a halogen-free flame-retardant partially crosslinked compound suitable for thin wall automotive cables and low voltage insulation. To be used with 1-2% of catalyst MAC/202. The material doesn’t pass abrasion test on cables sized less than 0.75 mm² having 0.25 mm thickness. Certify: SAE J1127/J1128,FIAT 7.Z8220 T3 -T3 S,ISO 6722 Class C,LV 112&& |
| Product Description | |
|---|---|
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Crosslinked,Halogen free,Flame Characteristics |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 1.0 to 2.0 | g/10min | ASTM D1238 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat aging | |||
| 175℃ | No Crack | IEC 60811 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Operating temperature | -40 to 125 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| Halogen Content | < 0.100 | % | IEC 60754-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 51 | ASTM D2240 | |
| tensile strength | |||
| yield | > 15.0 | MPa | IEC 60811 |
| Tensile strain | |||
| fracture | > 200 | % | IEC 60811 |
| abrasion resistance | |||
| 250.0 µm | > 3.5E+2 | Cycles | LV 112 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Barrel 1 zone temperature | 170 | °C | |
| Barrel 2 zone temperature | 185 | °C | |
| Barrel 3 zone temperature | 190 | °C | |
| Barrel 4 zone temperature | 210 | °C | |
| Barrel 5 zone temperature | 220 | °C | |
| Nozzle temperature | 225 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.75mm² Size |
| 3. 1 hr on Mandrel |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |