| About |
|---|
| FRAGOM : is our brand of thermoplastic compounds having a very low flame propagation under fire conditions. Our Fragom is PVC free and also heavy-metals free. FRAGOM PR/04 AFKK N : is designed to extrude both cable insulation and sheathing at high speed without any migration risks as it is completely free of plasticizers. Fragom PR/04 AFKKN meets the Australian Standard AS/NZ3808.2000 Insulation Type HFI-75-TP,HFI-90-TP,HFI-110-TP Sheathing Type HFS-75-TP,HFS-90-TP,HFS-110-TP Certify : CEI2011 M1,VDE0207HM4(K=0,7),BS7655 LTS 3-4&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Low to no mobility |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 160℃，21.6kg | 6.0 to 12 | g/10min | ASTM D1238 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| Changes in tensile stress during fracture in air | |||
| 110℃，168 hr | < 25 | % | IEC 60811 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot press test | |||
| 6 h at 90℃Penetration | < 40 | % | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 50 Hz | 4.10 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 30 | % | ASTM D2863 |
| Halogen Content | 0 | % | IEC 60754-1 |
| Temperature index | |||
| burning | > 300 | ℃ | NES 715 |
| Corrosive gases in flue gas | |||
| pH | > 4.50 | IEC 60754-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | > 10.0 | BS 6469 99.1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 53 | ASTM D2240 | |
| tensile strength | > 10.0 | MPa | IEC 60811 |
| Tensile strain | |||
| fracture | > 170 | % | IEC 60811 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 130 | °C | |
| Barrel 2 zone temperature | 145 | °C | |
| Barrel 3 zone temperature | 160 | °C | |
| Barrel 4 zone temperature | 180 | °C | |
| Head temperature | 185 | °C | |
| Nozzle temperature | 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 21% O2 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |