| About |
|---|
| FRIANYL® A3 GF20 V2XI is a Polyamide 66 (Nylon 66) compound, 20% glass fiber reinforced, flame retardant with halogens, free from antimony trioxide, PBB and PBDE, UL listed V2. It is VDE certified. This compound is intended for injection molding. FRIANYL® A3 GF20 V2XI is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,No antimony,Halogenated,V-2,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃ | 0.80 | % | ISO 294-4 |
| MD：23℃ | 0.40 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 0.70 | % | ISO 62 |
| Saturation, 23 ℃ | 5.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6700 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 126 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 35 | kJ/m² | ISO 179/1eU |
| 23℃ | 45 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 6.5 | kJ/m² | ISO 180-A |
| 23℃ | 7.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| Continuous use temperature | 130 | ℃ | IEC 60216 |
| Ball pressure test | IEC 60695-10-2 | ||
| 125℃ | 通过 | IEC 60695-10-2 | |
| 165℃ | 通过 | IEC 60695-10-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm | 21 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| 3.20 mm, solution A | 375 | V | IEC 60112 |
| Needle flame test | IEC 60695-11-5 | ||
| 1.00 mm | 通过 | IEC 60695-11-5 | |
| 2.00 mm | 通过 | IEC 60695-11-5 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-2 | UL 94 | |
| 0.80 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 900 | ℃ | IEC 60695-2-13 |
| 3.2 mm | 900 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 34 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20000 hr |
| 3. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |