| About |
|---|
| Examples of application Automobile parts (Electrical components etc.) Heat-resistant, flame-resistant electrical parts Relays Microswitches Light electrical bobbins Measuring equipment parts Sealed devices Other Properties Arc resistance Tracking resistance&& |
| Product Description | |
|---|---|
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Arc resistance,Heat Resistance, Good,Electric mark |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.73 | g/cm³ | JIS K7112 |
| Shrinkage rate | 0.40 to 0.60 | % | JIS K6911 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 to 0.15 | % | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.9 to 4.4 | kJ/m² | JIS K7111 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 2.6E-5 | 1/℃ | |
| Hot deformation temperature | 200 to 210 | ℃ | JIS K7191-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 10 to 11 | kV/mm | JIS K6911 |
| Arc resistance | 183 | sec | |
| Compared to the leakage tracing index | 180 | V | |
| insulation resistance | |||
| After boiling | 1.0E+9 to 1.0E+10 | ohms | |
| at ordinary state | 1.0E+10 to 1.0E+11 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.51 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Free Ammonia | < 3.0E-3 | % | JIS K7230 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 108 | JIS K6911 | |
| tensile strength | 59.0 to 78.0 | MPa | JIS K6911 |
| Bending modulus | 10800 to 12700 | MPa | JIS K7171 |
| bending strength | 109 to 127 | MPa | JIS K7171 |
| compressive strength | 176 to 196 | MPa | JIS K6911 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |