| About |
|---|
| Examples of application Switches, relays, sockets, coil bobbins, relays, terminal strips, connectors, power switches, compact breakers, plug pipes, ignition coil caps Other properties: Mechanical properties&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.90 to 1.94 | g/cm³ | JIS K6911 |
| Shrinkage rate | 0.70 to 0.90 | % | JIS K6911 |
| Water absorption rate | |||
| boiling | 0.15 to 0.25 | % | JIS K6911 |
| 23℃，24hr | 0.020 to 0.050 | % | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 to 7.5 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 230 to 260 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 13 to 15 | kV/mm | JIS K6911 |
| Dielectric constant | |||
| 1 MHz | 5.00 to 5.50 | JIS K6911 | |
| Dissipation factor | |||
| 1 MHz | 0.015 to 0.035 | JIS K6911 | |
| Arc resistance | > 180 | sec | JIS K6911 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| insulation resistance | |||
| After boiling | 1.0E+12 to 1.0E+14 | ohms | |
| at ordinary state | 1.0E+14 to 1.0E+15 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.79 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 95 to 100 | JIS K6911 | |
| tensile strength | 59.0 to 78.0 | MPa | JIS K6911 |
| Bending modulus | 14000 to 16000 | MPa | JIS K6911 |
| bending strength | 127 to 147 | MPa | JIS K6911 |
| compressive strength | 176 to 225 | MPa | JIS K6911 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |