| About |
|---|
| Product Details: Ultra high performance lubricated polymer, carbon fiber, PTFE, graphite and MoS 2 filled in Polyether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Black in color. Application Areas: Suitable for high temperature application, where higher strength & stiffness in load- bearing application. Excellent wear resistance. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.&& |
| Product Description | |
|---|---|
| Generic | PEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good disinfection,Good liquidity,Food contact compliance,High Heat Resistance,Hypocrystalline,Good wear resistance,Solvent resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | |
| Shrinkage rate | |||
| MD | 0.11 | % | |
| TD | 0.50 | % | |
| Water absorption rate | |||
| balance | 0.050 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 45 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 610 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 349 | ℃ | ASTM D648 |
| Continuous use temperature | 280 | ℃ | UL 746B |
| Glass transition temperature | 152 | ℃ | ASTM D3418 |
| Melting temperature | 372 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+9 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 91 | ASTM D2240 | |
| Rockwell hardness | |||
| M-level | 106 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 11500 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 140 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.5 to 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 10500 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 210 | MPa | ASTM D790 |
| friction coefficient | 0.17 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Nozzle temperature | 420 | °C | |
| Processing (melt) temperature | 390 to 420 | °C | |
| Mold temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 410°C nozzle, 220°C Mold |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |