| Product Details: Ultra high Performance thermoplastic polymer, virgin, semicrystalline granules suitable for Injection Molding, easy flow, Beige in color. Application Areas: Suitable for high temperature application, high wear & abrasion resistance, high chemical resistance is required & for metal replacement with plastics etc.&& |
| Product Description | |
|---|---|
| Generic | PEK |
| Material Status | Commercial: Active |
| Features | Good liquidity,High Heat Resistance,Hypocrystalline,Good wear resistance,Solvent resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | No Break | ASTM D256 | |
| 23℃ | 35 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 175 | ℃ | ASTM D648 |
| Continuous use temperature | 280 | ℃ | UL 746B |
| Glass transition temperature | 152 | ℃ | ASTM D3418 |
| Melting temperature | 372 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 87 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 4300 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 90.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 to 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 4300 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 163 | MPa | ASTM D790 |
| compressive strength | 130 | MPa | ASTM D695 |
| Rockwell hardness | |||
| M-level | 98 | ASTM D785 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Spiral flow length | 53.0 | cm | ASTM D3123 |
| Shrinkage rate | |||
| TD | 1.4 | % | |
| MD | 1.1 | % | |
| Water absorption rate | |||
| balance | 0.070 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 200 to 250 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Nozzle temperature | 400 | °C | |
| Processing (melt) temperature | 390 to 400 | °C | |
| Mold temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 400°C nozzle, 220°C Mold |
| 3. 400°C nozzle, 210°C Mold |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |