| About |
|---|
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.2 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.2kg | 9 – 11 | g/10min | ISO 1133 |
| Shrinkage rate | 0.5 – 0.7 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturated, in water at 23 ℃ | 0.3 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.2 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | 65 | Kj/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| 5Kg，50℃/hr | 142 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8Mpa | 125 | ℃ | ISO 75-A |
| 0.45Mpa | 136 | ℃ | ISO 75-A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2350 | MPa | ISO 527 |
| tensile strength | |||
| 50 mm/min | 63 | MPa | ISO 527 |
| stretch forming | 6 | % | ISO 527 |
| Tensile strain | |||
| fracture | 115 | % | ISO 527 |
| bending strength | 92 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |