| About |
|---|
| Product Details: Ultra high performance thermoplastic polymer, unfilled Polyether Ketone Ketone (PEKK), semicrystalline granules suitable for injection molding and stock shapes extrusion, standard flow, Brown in color. Application Areas: Suitable for high temperature applications, with high compressive strength & abrasion resistance, high chemical resistance & oil resistance etc.&& |
| Product Description | |
|---|---|
| Generic | PEKK |
| Material Status | Commercial: Active |
| Features | Good liquidity,High Heat Resistance,Hypocrystalline,Good wear resistance,Grease resistance,Solvent resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 1.0 | % | |
| Water absorption rate | |||
| balance | 0.050 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 88 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 4000 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 10 to 15 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 4300 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 180 | MPa | ASTM D790 |
| Compression modulus | 2100 | MPa | ASTM D695 |
| compressive strength | |||
| 23℃ | 132 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 50 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 189 | ℃ | ASTM D648 |
| Continuous use temperature | 300 | ℃ | UL 746B |
| Glass transition temperature | 176 | ℃ | ASTM D3418 |
| Melting temperature | 396 | ℃ | ASTM D3418 |
| thermal stability | |||
| Haake | 20 | min |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Nozzle temperature | 420 | °C | |
| Processing (melt) temperature | 390 to 420 | °C | |
| Mold temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 420°C nozzle, 220°C Mold |
| 3. GSRF 05/420°C, 60 rpm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |