| About |
|---|
| GAPEX® HT RNP23MU02BK是一种聚酰胺 + PP（尼龙+PP）材料,含有的填充物为23% 玻璃织物增强材料。 该产品在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货,加工方式为:注射成型。 GAPEX® HT RNP23MU02BK的主要特性为:耐热。&& |
| Product Description | |
|---|---|
| Supplier | Ferro |
| Generic | PA+PP |
| Material Status | Commercial: Active |
| Features | High Heat Resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD | 1.1 | % | ASTM D955 |
| MD | 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 114 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 5.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% secant, 23 ℃ | 5480 | MPa | ASTM D790 |
| Tangent, 23 ℃ | 5580 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 162 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 830 | J/m | ASTM D4812 |
| 23℃ | 120 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 0.565 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 241 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 252 | ℃ | ASTM D648 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |