| About |
|---|
| GARAFLEX E 4771-A8 OR-1 LCF IS A 105°C RATED, LEAD FREE, FLAME RETARDED, FLEXIBLE JACKETING COMPOUND.&& |
| Product Description | |
|---|---|
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Flame Characteristics,Lead content is low to none |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 to 1.44 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 75 to 81 | ||
| Shore A, 15 seconds | 65 to 71 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 0.762 mm | 13.1 | MPa | |
| 1.91 mm | 12.4 | MPa | |
| Tensile strain | ASTM D412 | ||
| Fracture, 1.91 mm | 340 | % | |
| Fracture, 0.762 mm | 320 | % |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 136℃，168 hr | -8.0 | % | UL Unspecified |
| The rate of change in ultimate elongation in air | |||
| 136℃，168 hr | -18 | % | UL Unspecified |
| The rate of change in tensile strength | |||
| 60 ℃, 168 hr, in ASTM # 2 oil | -5.0 | % | UL Unspecified |
| Change rate of ultimate elongation | |||
| 60 ℃, 168 hr, in ASTM # 2 oil | -15 | % | UL Unspecified |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -24.0 | ℃ | ASTM D746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | |||
| 3.18 mm | 34 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 149 | °C | |
| Barrel 2 zone temperature | 154 | °C | |
| Barrel 3 zone temperature | 160 | °C | |
| Barrel 4 zone temperature | 166 | °C | |
| Barrel 5 zone temperature | 171 | °C | |
| Connector temperature | 171 | °C | |
| Melt temperature | 163 to 171 | °C | |
| Nozzle temperature | 171 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Thickness: 30 mil |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |