| About |
|---|
| GARAFLEX O 9949RA IS A PBB, PBBE AND PBBO FREE, 105C DEGREE, FLAME RETARDED, OLEFINIC THERMOPLASTIC ELASTOMER INTENDED FOR FLAT RIBBON PRIMARY AND HEAT TRACING CABLE.&& |
| Product Description | |
|---|---|
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 to 1.19 | g/cm³ | ASTM D792 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 0.762 mm | 8.96 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 0.762 mm | 190 | % | ASTM D412 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s D | 56 to 62 | ASTM D2240 | |
| Shore D, 15 seconds | 46 to 52 | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -50.0 | ℃ | ASTM D746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | ASTM D150 | ||
| 23 ℃，1 MHz | 2.36 | ASTM D150 | |
| 23 ℃，1.00 GHz | 2.45 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 23℃，1 MHz | 5.0E-4 | ASTM D150 | |
| 23℃，1 GHz | 1.0E-4 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | |||
| 3.18 mm | 29 | % | ASTM D2863 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 166 | °C | |
| Barrel 2 zone temperature | 188 | °C | |
| Barrel 3 zone temperature | 193 | °C | |
| Barrel 4 zone temperature | 199 | °C | |
| Barrel 5 zone temperature | 204 | °C | |
| Connector temperature | 204 | °C | |
| Melt temperature | 204 to 216 | °C | |
| Nozzle temperature | 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |