| GATONE™ 5630GF is a Polyetheretherketone (PEEK) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of GATONE™ 5630GF: Flame Rated. Typical application of GATONE™ 5630GF: Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.080 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 95 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, injection molded | 20.0 | ℃ | ASTM D648 |
| Continuous use temperature | 0.00300 | ℃ | ASTM D794 |
| Glass transition temperature | 2.90 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | 150 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 | |
| Extreme oxygen index | 45 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 102 | ASTM D785 | |
| Tensile modulus | |||
| 23 ℃, injection molding | 10000 | MPa | ASTM D638 |
| tensile strength | |||
| 23 ℃, injection molding | 160 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, injection molding | 2.5 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, injection molding | 10000 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, injection molding | 260 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |