| Product Details: Ultra high performance thermoplastic polymer, 30% glass fiber reinforced in PBI PEK Blend, semi-crystalline granules suitable for injection molding as well as extrusion, easy flow, dark green in color. Application Areas: Suitable for high temperature applications under extremely high load, Excellent wear resistance, suitable for semiconductor applications and plasma handling equipments.&& |
| Product Description | |
|---|---|
| Generic | PBI |
| Material Status | Commercial: Active |
| Features | Good liquidity,High Heat Resistance,Hypocrystalline,Good wear resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | |
| Shrinkage rate | |||
| TD | 0.58 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| balance | 0.24 | % | ASTM D570 |
| Spiral flow length | 4.50 | cm | ASTM D3123 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 45 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 310 | ℃ | ASTM D648 |
| Continuous use temperature | 300 | ℃ | UL 746B |
| Glass transition temperature | 152 | ℃ | ASTM D3418 |
| Melting temperature | 372 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heating reduction | Internal Method | ||
| 5% Weight Loss in Air | 580 | ℃ | Internal Method |
| 5% Weight Loss in Nitrogen | 570 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 95 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 13500 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 167 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.7 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 13600 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 282 | MPa | ASTM D790 |
| Rockwell hardness | |||
| A-level | 30 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Nozzle temperature | 445 | °C | |
| Processing (melt) temperature | 400 to 445 | °C | |
| Mold temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 445°C nozzle, 220°C Mold |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |