GECET™ F-300

About
GECET TM resins are light weight, and high strength expandable interpolymers that withstand high temperatures. These resins are used in the automotive, bicycle helmet, and other industries where it is required to manage the impact energy. For the same stiffness, a part made from GECET TM resins is 20% and 40% lighter than EPP and PU Foam respectively. Usually a part with the same stiffness made from GECET TM resins costs less than EPP and PU foam part. GECET TM resins parts can be molded for a density range of 2.25 to 20.00 pounds per cubic foot (pcf) enabling the designer to custom-tailor GECET TM resins to specific applications. GECET TM resins may be used for applications that require an end use temperature up to 250o F. All GECET TM resins are black and micro-pelletized with a particle size of 0.6 – 1.2 mm prior to pre-expansion.&&

About

GECET TM resins are light weight, and high strength expandable interpolymers that withstand high temperatures. These resins are used in the automotive, bicycle helmet, and other industries where it is required to manage the impact energy. For the same stiffness, a part made from GECET TM resins is 20% and 40% lighter than EPP and PU Foam respectively. Usually a part with the same stiffness made from GECET TM resins costs less than EPP and PU foam part. GECET TM resins parts can be molded for a density range of 2.25 to 20.00 pounds per cubic foot (pcf) enabling the designer to custom-tailor GECET TM resins to specific applications. GECET TM resins may be used for applications that require an end use temperature up to 250o F. All GECET TM resins are black and micro-pelletized with a particle size of 0.6 – 1.2 mm prior to pre-expansion.&&

Product Description
Supplier	Fagerdala
Generic	PS (EPS)
Material Status	Commercial: Active
Features	Good Rigidity,Foaming performance,High Heat Resistance,HB
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
bending strength			ASTM C203
—	2.23	MPa
—	1.48	MPa
compressive strength			ASTM D1621
10% strain	1.02	MPa
10% strain	0.738	MPa
15% strain	1.10	MPa
15% strain	0.793	MPa
20% strain	1.16	MPa
20% strain	0.834	MPa

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
7.62 mm	HBF		UL 94

Flame retardant rating – MVSS	Nominal value	Unit	Test method
—	Pass
—	Pass

Supplementary information	Nominal value	Test method
Thermal Resistance – R-value		ASTM C518
2.54 cm	3.40
2.54 cm	3.30

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.