| About |
|---|
| ASA, excellent weatherable, extrusion grade&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low Gloss |
| Availabilitys | North America,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 6.4 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.55 to 0.63 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1840 | MPa | ASTM D638 |
| Tensile modulus | 1800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 31.0 | MPa | ISO 527-2/50 |
| fracture | 30.0 | MPa | ASTM D638 |
| yield | 39.0 | MPa | ASTM D638 |
| yield | 39.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 38 | % | ASTM D638 |
| fracture | 23 | % | ISO 527-2/50 |
| yield | 3.4 | % | ISO 527-2/50 |
| yield | 3.5 | % | ASTM D638 |
| Bending modulus | 1800 | MPa | ISO 178 |
| 50 mm span | 1860 | MPa | ASTM D790 |
| bending strength | 56.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 57.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 1.2 | J/m | ASTM D256 |
| 23℃ | 8.4 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 3.8 | kJ/m² | ISO 180-1A |
| 23℃ | 26 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 4.50 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 77.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 74.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 9 |
| B50 | 100 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 2.0E-4 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 1.4E-4 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Barrel 1 zone temperature | 204 to 216 | °C | |
| Barrel 2 zone temperature | 216 to 232 | °C | |
| Barrel 3 zone temperature | 221 to 238 | °C | |
| Barrel 4 zone temperature | 227 to 243 | °C | |
| Connector temperature | 227 to 243 | °C | |
| Melt temperature | 227 to 254 | °C | |
| Nozzle temperature | 227 to 243 | °C | |
| Calibration temperature, first time | 16 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 |
| 8. 80*10*4 mm |
| 9. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |