改进的ASA / PC混合树脂,高流动性,改善紫外线性能 |
Product Description | |
---|---|
Supplier | SABIC |
Generic | ASA+PC |
Material Status | Commercial: Active |
Features | High liquidity |
Availabilitys | Asia Pacific |
Technical Data | |||
---|---|---|---|
MECHANICAL | Nominal value | Unit | Test method |
tensile strength | |||
Fracture, Type I, 5 mm/min | 49 | MPa | ASTM D638 |
Fracture, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
Fracture, 5 mm/min | 46 | MPa | ISO 527 |
Fracture, 50 mm/min | 47 | MPa | ISO 527 |
Yield, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
Yield, Type I, 5 mm/min | 60 | MPa | ASTM D638 |
Yield, 5 mm/min | 61 | MPa | ISO 527 |
Yield, 50 mm/min | 66 | MPa | ISO 527 |
Tensile strain | |||
Fracture, Type I, 5 mm/min | 58 | % | ASTM D638 |
Fracture, Type I, 50 mm/min | 31 | % | ASTM D638 |
Fracture, 5 mm/min | 50 | % | ISO 527 |
Fracture, 50 mm/min | 21 | % | ISO 527 |
Yield, Type I, 50 mm/min | 4 | % | ASTM D638 |
Yield, Type I, 5 mm/min | 4 | % | ASTM D638 |
Yield, 50 mm/min | 4 | % | ISO 527 |
Yield, 5 mm/min | 4 | % | ISO 527 |
Tensile modulus | |||
5 mm/min | 2680 | MPa | ASTM D638 |
1 mm/min | 2680 | MPa | ISO 527 |
bending strength | |||
Yield, 2 mm/min | 97 | MPa | ISO 178 |
Bending modulus | |||
2 mm/mim | 2742 | MPa | ISO 178 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | |||
23℃ | 330 | J/m | ASTM D256 |
Impact strength of cantilever beam notch | |||
-30℃ | 90 | J/m | ASTM D256 |
Multiaxial impact | 85 | J | ISO 6603 |
Impact strength of cantilever beam notch | |||
23℃,80*10*4 | 13 | kJ/m² | ISO 180-1A |
40℃,80*10*4 | 12 | kJ/m² | ISO 180-1A |
Charpy Notched Impact Strength | |||
23 ℃, 80 * 10 * 4, 62mm span | 13 | kJ/m² | ISO 179/1eA |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Linear coefficient of thermal expansion | |||
TD:-40~40℃ | 6.3E-05 | 1/℃ | ISO 11359-2 |
MD:-40~40℃ | 6.3E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp | 96 | ℃ | ISO 306 |
Vicat Softening Temp | 98 | ℃ | ISO 306 |
Hot deformation temperature | |||
0.45 MPa, 64 mm span | 90 | ℃ | ISO 75/Bf |
1.8 MPa, 64 mm span | 81 | ℃ | ISO 75/Af |
PHYSICAL | Nominal value | Unit | Test method |
---|---|---|---|
Density | 1.18 | g/cm³ | ISO 1183 |
Melt Volume Rate | |||
260℃,2.16 kg | 30 | cm³/10min | ISO 1133 |
Apparent viscosity of melt | |||
260℃,1500 sec-1 | 105 | Pa-s | ISO 11443 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
94V-1 flame level | 1 | mm | UL 94 (SABIC-IP) |
Process Conditions | |||
---|---|---|---|
injection molding | Nominal value | Unit | Test method |
Drying temperature | 80 – 90 | °C | |
Drying time | 2 – 4 | hrs | |
Maximum water content | 0.02 | % | |
Melt temperature | 230 – 270 | °C | |
Nozzle temperature | 220 – 260 | °C | |
Front Section Zone 3 Temperature | 230 – 270 | °C | |
Temperature in Zone 2 of the middle section | 220 – 260 | °C | |
Temperature in Zone 1 of the rear section | 200 – 230 | °C | |
Hopper temperature | 60 – 80 | °C | |
Mold temperature | 50 – 70 | °C |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |