GELOY™ FXW751SK resin

About
Sparkle Metallic VisualFx ASA+PC Resin – Weatherable, High Heat & Impact Resin&&

Product Description
SupplierSABIC
GenericASA+PC
Material StatusCommercial: Active
FeaturesWeather resistance is good,High impact resistance,High Heat Resistance
AvailabilitysNorth America,Asia Pacific,Europe
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.16g/cm³ASTM D792
Density1.16g/cm³ISO 1183
Melt Flow Rate
220℃,10.0kg8.3g/10minASTM D1238
Melt Volume Rate
220℃,10 kg7.20cm³/10minISO 1133
Shrinkage rate
MD:3.2 mm0.50 to 0.70%Internal Method
Water absorption rate
Saturation, 23 ℃1.0%ISO 62
Equilibrium, 23 ℃, 50% RH0.25%ISO 62

MECHANICALNominal valueUnitTest method
Tensile modulus2690MPaASTM D638
Tensile modulus2900MPaISO 527-1-2
tensile strength
fracture48.0MPaISO 527-2/50
fracture48.0MPaASTM D638
yield60.2MPaISO 527-2/50
yield62.0MPaASTM D638
Tensile strain
fracture49%ASTM D638
fracture77%ISO 527-2/50
yield4.2%ISO 527-2/50
yield4.2%ASTM D638
Bending modulus2700MPaISO 178
50 mm span2750MPaASTM D790
bending strength78.0MPaISO 178
bending strength
Yield, 50 mm span95.0MPaASTM D790

IMPACTNominal valueUnitTest method
Charpy Notched Impact Strength
23℃17kJ/m²ISO 179/1eA
Impact strength of cantilever beam notch ASTM D256
-30℃50J/mASTM D256
23℃170J/mASTM D256
Impact strength of cantilever beam notch ISO 180/1A
-30℃5.2kJ/m²ISO 180-1A
23℃17kJ/m²ISO 180-1A
Dart impact equipped with measuring instruments
23℃,Total Energy43.0JASTM D3763

THERMALNominal valueUnitTest method
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span93.5ISO 75-2/Af
1.8 MPa, unannealed, 3.2 mm89.0ASTM D648
Vicat Softening Temp105ASTM D1525 10
Vicat Softening Temp 
B50108ISO 306
B120109ISO 306/B120
Linear coefficient of thermal expansion
TD:-40~40℃7.2E-51/℃ASTM E831
TD:-40~40℃7.2E-51/℃ISO 11359-2
MD:-40~40℃7.2E-51/℃ISO 11359-2
MD:-40~40℃7.2E-51/℃ASTM E831

Process Conditions
injectionNominal valueUnitTest method
Drying temperature93 to 104°C
Drying time3.0 to 4.0hr
Drying time, maximum8.0hr
Recommended maximum moisture content0.040%
Recommended injection volume40 to 80%
Barrel rear temperature238 to 254°C
Barrel middle temperature243 to 260°C
Barrel front temperature249 to 266°C
Nozzle temperature243 to 266°C
Processing (melt) temperature260 to 277°C
Mold temperature54 to 71°C
Back pressure0.345 to 1.03MPa
Screw speed30 to 80rpm
Vent depth0.038 to 0.076mm

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.20 in/min
3. Type I, 2.0 in/min
4. 0.051 in/min
5. 0.079 in/min
6. Yield
7. 80*10*4 sp=62mm
8. 80*10*4
9. 80*10*4 mm
10. Rate B (120°C/h), Loading 2 (50 N)
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.