| About |
|---|
| GELOY HRA222F is a multi-purpose, chlorine and bromine free flame retardant ASA-PC alloy for injection moulding processes. This grade has a F1 rating according UL746C. Typical properties as measured on natural material.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.60 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Weathering resistance | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2590 | MPa | ASTM D638 |
| Tensile modulus | 2520 | MPa | ISO 527-1-2 |
| tensile strength | ASTM D638 | ||
| yield | 59.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 62.0 | MPa | ISO 527-2/5 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| tensile strength | ASTM D638 | ||
| fracture | 66.0 | MPa | ASTM D638 |
| fracture | 56.0 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 51.0 | MPa | ISO 527-2/5 |
| fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | ASTM D638 | ||
| yield | 4.2 | % | ASTM D638 |
| yield | 4.3 | % | ASTM D638 |
| Tensile strain | |||
| yield | 4.3 | % | ISO 527-2/5 |
| yield | 4.4 | % | ISO 527-2/50 |
| Tensile strain | ASTM D638 | ||
| fracture | > 100 | % | ASTM D638 |
| fracture | > 100 | % | ASTM D638 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2/5 |
| fracture | > 50 | % | ISO 527-2/50 |
| Bending modulus | 2520 | MPa | ISO 178 |
| bending strength | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 0℃ | 290 | J/m | ASTM D256 |
| 23℃ | 390 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 0℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 17 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 88.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 100 mm span | 99.0 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| A50 | 111 | ℃ | ISO 306/A50 |
| B50 | 102 | ℃ | ISO 306 |
| B120 | 104 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD | ISO 11359-2 | ||
| MD：-30~80℃ | 6.9E-5 | 1/℃ | ISO 11359-2 |
| -30 to 80 ℃ | 7.1E-5 | cm/cm/℃ | ISO 11359-2 |
| 23 to 80 ℃ | 7.5E-5 | cm/cm/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 29 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 200 to 230 | °C | |
| Barrel middle temperature | 220 to 260 | °C | |
| Barrel front temperature | 230 to 270 | °C | |
| Nozzle temperature | 220 to 260 | °C | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 2.0 in/min |
| 5. Type I, 0.20 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 |
| 10. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |