| About |
|---|
| ASA+PC may contain up to 20% post-industrial recycle. Excellent flow, weatherability, toughness and high heat for exterior uses.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good liquidity,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 10 | g/10min | |
| 230℃，3.80kg | 22 | g/10min | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 69 | J/m | |
| 23℃ | 300 | J/m | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 22.6 | J | |
| 23℃，Total Energy | 33.9 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 107 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | |
| Vicat Softening Temp | 121 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 9.0E-5 | 1/℃ | |
| TD：-40~40℃ | 8.1E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | 39 | mm/min | ISO 3795 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 98 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 | |
| Tensile modulus | 3030 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 60.7 | MPa | |
| fracture | 44.1 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 3.7 | % | |
| fracture | 36 | % | |
| Bending modulus | |||
| 50 mm span | 2550 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 86.2 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 87.8 to 98.9 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |