| About |
|---|
| PC/ASA. Excellent weatherability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Quick molding cycle,Good color stability,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 6.8 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 18 | g/10min | ASTM D1238 |
| 280℃，3.80kg | 31 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.24 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 37 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 64 | J/m | ASTM D256 |
| 23℃ | 170 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 21 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 33.9 | J | ASTM D3763 |
| 23℃，Total Energy | 39.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 93.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 6.4 mm | 90.6 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 107 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 103 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 109 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-20：150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：-20~150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 90 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 44.0 | MPa | ISO 527-2/50 |
| yield | 58.0 | MPa | ISO 527-2/50 |
| yield | 59.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| fracture | 64 | % | ISO 527-2/50 |
| yield | 4.1 | % | ISO 527-2/50 |
| Bending modulus | 2500 | MPa | ISO 178 |
| 50 mm span | 2590 | MPa | ASTM D790 |
| bending strength | 75.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 88.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 88 to 99 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 232 to 249 | °C | |
| Barrel middle temperature | 238 to 254 | °C | |
| Barrel front temperature | 243 to 260 | °C | |
| Nozzle temperature | 238 to 254 | °C | |
| Processing (melt) temperature | 254 to 271 | °C | |
| Mold temperature | 54 to 71 | °C | |
| Back pressure | 0.345 to 1.03 | MPa | |
| Screw speed | 30 to 80 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Drying temperature | 88 to 99 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 221 to 232 | °C | |
| Barrel 2 zone temperature | 232 to 243 | °C | |
| Barrel 3 zone temperature | 243 to 254 | °C | |
| Barrel 4 zone temperature | 254 to 266 | °C | |
| Connector temperature | 254 to 266 | °C | |
| Melt temperature | 254 to 271 | °C | |
| Nozzle temperature | 254 to 266 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.051 in/min |
| 4. 0.079 in/min |
| 5. Yield |
| 6. 80*10*4 sp=62mm |
| 7. 80*10*4 |
| 8. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |