| About |
|---|
| PC/ASA. Excellent weatherability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High Heat Resistance,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| 260℃，5.0kg | 14 | g/10min | ASTM D1238 |
| 280℃，3.80kg | 24 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.25 | % | ASTM D570 |
| Weathering resistance | f2 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 32 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 80 | J/m | ASTM D256 |
| 23℃ | 320 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 33 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 30.5 | J | ASTM D3763 |
| 23℃，Total Energy | 47.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 98.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 6.4 mm | 104 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 116 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 116 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 113 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-20：150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：-20~150℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM C177 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 94 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ISO 527-2/50 |
| yield | 57.0 | MPa | ISO 527-2/50 |
| yield | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 130 | % | ISO 527-2/50 |
| fracture | 25 | % | ASTM D638 |
| yield | 4.5 | % | ISO 527-2/50 |
| Bending modulus | 2500 | MPa | ISO 178 |
| 50 mm span | 2520 | MPa | ASTM D790 |
| bending strength | 75.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 88.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 93 to 104 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 238 to 254 | °C | |
| Barrel middle temperature | 243 to 260 | °C | |
| Barrel front temperature | 249 to 266 | °C | |
| Nozzle temperature | 243 to 266 | °C | |
| Processing (melt) temperature | 260 to 277 | °C | |
| Mold temperature | 54 to 71 | °C | |
| Back pressure | 0.345 to 1.03 | MPa | |
| Screw speed | 30 to 80 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Drying temperature | 88 to 99 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 227 to 238 | °C | |
| Barrel 2 zone temperature | 238 to 249 | °C | |
| Barrel 3 zone temperature | 249 to 260 | °C | |
| Barrel 4 zone temperature | 260 to 271 | °C | |
| Connector temperature | 260 to 271 | °C | |
| Melt temperature | 260 to 282 | °C | |
| Nozzle temperature | 260 to 271 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2,0 in/min |
| 3. 0,051 in/min |
| 4. 0,079 in/min |
| 5. Yield |
| 6. 80*10*4 sp=62mm |
| 7. 80*10*4 |
| 8. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |