| GELOY XP7560 is a general purpose ASA/PC injection moulding grade, available in various colours.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.80 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 20 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 86.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 100 mm span | 102 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| A50 | 113 | ℃ | ISO 306/A50 |
| B50 | 102 | ℃ | ISO 306 |
| B120 | 107 | ℃ | ISO 306/B120 |
| Ball pressure test | IEC 60695-10-2 | ||
| 75℃ | Pass | IEC 60695-10-2 | |
| 95℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~60℃ | 9.5E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2460 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 43.0 | MPa | ISO 527-2/50 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 20 | % | ISO 527-2/50 |
| yield | 3.7 | % | ISO 527-2/50 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 82.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 111 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 92.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 220 to 250 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 240 to 270 | °C | |
| Nozzle temperature | 230 to 260 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 |
| 6. 120*10*4 mm |
| 7. Approximate maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |