| About |
|---|
| Genestar G1301A-M61 is a 30% glass reinforced and impact modified injection grade. Main feature of G1301A-M61 are; Higher elongation and impact strength Heat resistance Chemical resistance Examples of application are; Quick connector&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.90 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.19 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 175 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 8200 | MPa | ISO 178 |
| bending strength | 250 | MPa | ISO 178 |
| friction coefficient | 0.30 | JIS K7218 | |
| Wear amount | 15.0 | mg | JIS K7218 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 17 | kJ/m² | ISO 179-1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/Af |
| Glass transition temperature | 125 | ℃ | |
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. P=10kgf/cm² |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |