| About |
|---|
| The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. *’Halogen free’ follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Halogen free,Good wear resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | |
| Melt Flow Rate | |||
| 320℃，2.16kg | 46 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：1.0 mm | 0.20 | % | |
| TD：1.00 mm | 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 40 ℃, 95% RH | 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 165 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 9000 | MPa | ASTM D790 |
| bending strength | 210 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ASTM D648 |
| Glass transition temperature | 125 | ℃ | |
| Melting temperature | 306 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 30 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 10.0 GHz | 3.30 | ASTM D150 | |
| Dissipation factor | |||
| 10 GHz | 9.0E-3 | ASTM D150 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Rod flow length | |||
| 320℃，500.0 µm | 5.50 | cm | |
| Weld Elongation | 0.70 | % | ASTM D638 |
| Weld Strength | 47.0 | MPa | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 96 hrs |
| 3. 750kgf |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |