| About |
|---|
| The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. *’Halogen free’ follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | Low warping,High liquidity,Halogen free |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：1.0 mm | 0.50 | % | ASTM D995 |
| TD：1.00 mm | 0.05 | % | ASTM D995 |
| Water absorption rate | |||
| 40℃，95% RH | 1.10 | % | ASTM D570 |
| Melt Flow Rate | |||
| 320℃，2.16kg | 90.00 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 150 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.10 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 207 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 13000 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ASTM D648 |
| Melting temperature | 306 | ℃ | ASTM D4591 |
| Glass transition temperature | 125 | ℃ | ASTM D648 |
| Vicat Softening Temp |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 30 | KV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 96 hrs |
| 3. 750kgf |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |