| About |
|---|
| Genestar N1006A-M41 is impact modified unreinforced injection grade. Main feature of N1006A-M41 are; High elongation High impact strength Examples of application are; Retainers for quick connector Flexible band&& |
| Product Description | |
|---|---|
| Supplier | Kuraray |
| Generic | PA 9T |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,Good Tensile Strength |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.40 | % | ISO 294-4 |
| TD：2.0 mm | 1.50 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 50 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 20 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 70 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 1500 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 110 | ℃ | ISO 75-2/Af |
| Melting temperature | 300 | ℃ | ISO 11357-3 |
| Glass transition temperature | 125 | ℃ | ISO 11357-2 |
| Vicat Softening Temp |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. P=10kgf/cm² |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |