| About |
|---|
| Geon LC510 CPVC is an extrusion grade rigid compound. LC510 offers excellent chemical resistance and is designed for applications where enhanced resistance at elevated temperatures is needed. LC510 demonstrates ease of processing with excellent thermal stability.&& |
| Product Description | |
|---|---|
| Generic | CPVC |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Africa & Middle East ,Latin America,North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Falling impact resistance | |||
| 23℃ | 66.7 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 106 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 3.2 mm | 111 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 92.8 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 105 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds, 3.18 mm | 80 | ASTM D2240 | |
| Tensile modulus | |||
| 23 ℃, 3.18 mm, molded | 2250 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃, 3.18 mm, molded | 53.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.18 mm | 24 | % | ASTM D638 |
| Bending modulus | |||
| 23℃，3.18 mm | 2430 | MPa | ASTM D790 |
| bending strength | |||
| 23℃，3.18 mm | 79.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion molding | Nominal value | Unit | Test method |
| Melt Temperature | 191 to 199 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Procedure A, C.125 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |