| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Negative |
| Features | Impact modification,Ultra high liquidity |
| Availabilitys | Asia Pacific,North America,Latin America,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | ASTM D792 | |
| Spiral Flow | 112 | cm | |
| Molding Shrinkage | |||
| flow | 0.2-0.5 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength | |||
| yld | 41.4 | MPa | ASTM D638 |
| Elongation at Break | 35 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 66.9 | MPa | ASTM D790 |
| Shore hardness | 79 | Shore D | ASTM D2240 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| -18℃，3.18 mm | 110 | J/m | ASTM D256 |
| 0℃，3.18 mm | 270 | J/m | ASTM D256 |
| 23℃，3.18 mm | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 0.45 MPa | 72.2 | ℃ | ASTM D648 |
| 0.45 MPa | 75 | ℃ | ASTM D648 |
| 1.8 MPa | 68.9 | ℃ | ASTM D648 |
| 1.8 MPa | 72.8 | ℃ | ASTM D648 |
| Relative Temp Index(RTI) | |||
| elec | 90 | ℃ | UL746B |
| Imp | 85 | ℃ | UL746B |
| Str | 90 | ℃ | UL746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.75 mm | V-0 | UL 94 | |
| 1.5 mm | 5VA | UL 94 | |
| CSA Flammability | |||
| 1.6 mm | V-0 | ||
| 1.6 mm | 5VA |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melt Temperature | 199-210 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |