| About |
|---|
| Interior application for thick & thin gauge profile application.&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | V-0,Low Gloss |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe,Asia Pacific |
| Process Methods | Extrusion,Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D1638 |
| PVC unit classification | 12344 | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 70 | J/m | ASTM D256 |
| Falling impact resistance | ASTM D4226 | ||
| 23℃ | 53.8 | J/cm | ASTM D4226 |
| 23℃ | 102 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 74.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.7E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 81 | ASTM D2240 | |
| Tensile modulus | 2680 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 45.9 | MPa | ASTM D638 |
| Bending modulus | 2880 | MPa | ASTM D790 |
| bending strength | 84.1 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Melt Temperature | 191 to 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. Compression Molded |
| 4. Procedure A, C.125 Dart |
| 5. Procedure B, C.125 Dart |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |