| About |
|---|
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe,Latin America,Africa & Middle East ,North America |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 35.0 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 20 | % | ASTM D395 |
| Kappa’s modulus | ASTM D1043 | ||
| — | 81.4 | MPa | ASTM D1043 |
| -46℃ | 310 | MPa | ASTM D1043 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -42.2 | ℃ | ASTM D746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 70 | ASTM D2240 | |
| Shore A, 15 seconds | 64 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| fracture | 10.1 | MPa | ASTM D638 |
| 100% strain | 4.34 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 390 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 193 to 199 | °C | |
| Melt Temperature | 171 to 177 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |