| About |
|---|
| Geon™ Vinyl Rigid Extrusion L6256 is a Rigid Polyvinyl Chloride product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ Vinyl Rigid Extrusion L6256 include plumbing/piping/potable water and wire & cable. Characteristics include: Flame Rated Good Aesthetics High Flow&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Good surface appearance,5VA,High liquidity,V-0 |
| Availabilitys | Latin America,North America,Europe,Africa & Middle East ,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| PVC unit classification | 16364 | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| -18 ℃, 3.2mm, molded | 120 | J/m | ASTM D256-A |
| 0 ℃, 3.2mm, molded | 880 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, molded | 1200 | J/m | ASTM D256-A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -18℃，1.85 mm，brittle | 19.8 | J | ASTM D3763 |
| 0℃，1.85 mm，brittle | 21.9 | J | ASTM D3763 |
| 23℃，1.85 mm，ductile | 25.1 | J | ASTM D3763 |
| Falling impact resistance | ASTM D4226 | ||
| 23℃ | 66.7 | J/cm | ASTM D4226 |
| 23℃ | > 178 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 77.7 | ℃ | ASTM D648 |
| 0.45 MPa, annealed | 80.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 74.5 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 78.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.3E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.70 mm, all colors | V-0 | UL 94 | |
| 3.00 mm, all colors | 5VA | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ease of sizing | 良好 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 80 | ASTM D2240 | |
| Tensile modulus | 3060 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 42.3 | MPa | ASTM D638 |
| Bending modulus | 2660 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Melt Temperature | 177 to 188 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. all complete breaks |
| 4. all hinge breaks |
| 5. 10.8 ft/sec |
| 6. Procedure A, C.125 Dart |
| 7. Procedure B, C.125 Dart |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |