| About |
|---|
| Geon L7100 is recommended for whites and light pastel colors only. Not recommended for horizontal applications such as railing and decking except in white.&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | ASTM D792 |
| PVC unit classification | 15354 | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| 23 ℃, 3.2mm, molded | 570 to 810 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, molded | 130 | J/m | ASTM D256-A |
| Falling impact resistance | ASTM D4226 | ||
| 23℃ | 75.2 to 77.4 | J/cm | ASTM D4226 |
| 23℃ | 77.0 to 79.2 | J/cm | ASTM D4226 |
| 23℃，2.03 mm | 74.3 | J/cm | ASTM D4226 |
| 23℃，2.03 mm | 111 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 3.2 mm | 77.6 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 3.2 mm | 75.2 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm, molded | 75.4 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm, molded | 72.3 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.8E-5 | 1/℃ | ASTM D696 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ease of sizing | 可接受 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 73 | ASTM D2240 | |
| Tensile modulus | 2780 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 44.6 | MPa | ASTM D638 |
| Bending modulus | 3170 | MPa | ASTM D790 |
| bending strength | 81.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Melt Temperature | 182 to 193 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. Physical property based on commercial production sample. Compression molding of extruded strips. |
| 4. Physical property based on lab scale production sample. |
| 5. Procedure A, C.125 Dart |
| 6. Procedure B, C.125 Dart |
| 7. Procedure A, 1/8 conical |
| 8. Based on lab scale extrusion of commercial production sample. |
| 9. Procedure B, 0.125″ conical |
| 10. Annealed at 50 deg.C |
| 11. Annealed at 60 deg.C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |