| About |
|---|
| Geon™ Vinyl Rigid Extrusion L7801 is a Rigid Polyvinyl Chloride product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Outdoor Applications. Primary characteristic: impact resistant.&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Homopolymer,Moderate liquidity |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ASTM D792 |
| PVC unit classification | 1-41424-33-0000 | ASTM D4216 | |
| PVC unit classification | 16254 | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| 0 ℃, 3.2mm, molded | 200 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, molded | 1100 | J/m | ASTM D256-A |
| Falling impact resistance | ASTM D4226 | ||
| 0℃ | 40.5 | J/cm | ASTM D4226 |
| 23℃ | 52.0 | J/cm | ASTM D4226 |
| 23℃ | 178 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 76.1 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 3.2 mm | 78.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 71.1 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 73.9 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 6.3E-5 | 1/℃ | ASTM D696 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ease of sizing | 可接受 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 79 | ASTM D2240 | |
| Tensile modulus | 2900 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 41.3 | MPa | ASTM D638 |
| Bending modulus | 2960 | MPa | ASTM D790 |
| bending strength | 84.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| Melt Temperature | 182 to 193 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 3. Procedure A, C.125 Dart |
| 4. Procedure B, C.125 Dart |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |