| Geon™ Vinyl Rigid Molding M4821 is a Rigid Polyvinyl Chloride product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated Clarity High Flow&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Negative |
| Features | Good Clarity,V-0,High liquidity,5VA |
| Availabilitys | Africa & Middle East ,Europe,Asia Pacific,Latin America,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 2000 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| 0 ℃, 3.2mm, injection molding | 32 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, injection molding | 59 | J/m | ASTM D256-A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| 23 ℃, 3.18 mm, injection molded, Energy to Peak Load | 27.1 | J | ASTM D3763 |
| 23 ℃, 3.18 mm, injection molded, Total Energy | 75.9 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 3.2 mm | 67.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 65.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | V-0 | UL 94 | |
| 1.90 mm, all colors | 5VA | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3180 µm | 73.3 | % | ASTM D1003 |
| Haze | |||
| 3180 µm | 3.4 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ASTM D2240 | |
| Tensile modulus | 2780 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 51.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 21 | % | ASTM D638 |
| Bending modulus | 2740 | MPa | ASTM D790 |
| bending strength | 79.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 202 to 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure B |
| 3. Type I, 2.0 in/min |
| 4. 11.2 ft/sec |
| 5. CIE Illuminant C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |