| About |
|---|
| 优良机械性能,优异的尺寸稳定性,低翘曲&低收缩,20%玻纤含量 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good Dimensional Stability |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 10 mm/min | 115 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 10 mm/min | 2 | % | ISO 527-2 |
| bending strength | |||
| 2 mm/min | 155 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 7100 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 102 | ℃ | ISO 75-2 |
| Vicat Softening Temp | |||
| B120 | 112 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10^16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 2 mm in oil | 23 | KV/mm | IEC 60243-1 |
| other | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60-3.00 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.5 | kJ/m² | ISO 180 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Flow Rate | |||
| 220℃，10.0kg | 15 | g/10min | ISO 1133-1 |
| Shrinkage rate | 0.1-0.3 | % | ISO 2577 |
| Density | 1.22 | g/cm³ | ISO 1183-1 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melt temperature | 210-250 | °C | |
| Temperature of the rear section of the barrel | 190-215 | °C | |
| Temperature in the middle section of the barrel | 210-250 | °C | |
| Temperature of the front section of the material barrel | 220-260 | °C | |
| Mold temperature | 40-90 | °C | |
| Upper limit of processing temperature | 260 | °C | |
| Injection molding speed | 中速to高速 | ||
| Back pressure | 0-1000 | KPa | |
| Pre-drying | 80~90°C | undefined | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |