| PC/ABS Alloy : Non Reinforced Grade Classification: General purpose>Injection grade Characteristic: Injection grade, Ultra high impact Resistance Application GAC 265 resin gives exceptional impact strength even at low temperature and has a highheat resistance. Typical applications include automotive instrument panel, automotive interior and exteriortrim .This resin is particularly suited for thin wall molding.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High Heat Resistance,low-temperature impact resistance,HB |
| Availabilitys | Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，21.6kg | 30 to 40 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | > 55 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 118 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 to 125 | ASTM D785 | |
| tensile strength | |||
| Yield, 23 ℃ | > 53.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 95 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | > 1860 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | > 78.5 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 95 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | < 0.10 | % | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 230 to 260 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 260 to 270 | °C | |
| Processing (melt) temperature | 270 | °C | |
| Mold temperature | 70 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.11 in/min |
| 4. 6.4mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |