Glastic® 1603-2D

About
Glastic 1603-2D is a standoff insulator that is molded of UL recognized flame resistant fiberglass-reinforced thermoset polyester molding compound. Glastic 1603-2D features shatter resistance and closer height tolerances than commonly available in porcelain insulators. Moisture and heat resistance properties of Glastic 1603-2D are higher than those of conventional plastic insulators.&&

Product Description
Generic	热固性聚酯
Material Status	Commercial: Active
Features	Flame Characteristics,High Heat Resistance,Moisture resistance,V-0
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	17.2	MPa	ASTM D638
compressive strength	138	MPa	ASTM D695

Electrical performance	Nominal value	Unit	Test method
Arc resistance	180	sec	ASTM D495

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.