| About |
|---|
| A high hardness, multi-purpose thermoplastic elastomer featuring excellent compression set and high temperature performance. Globalene TPV 1050D BK can be processed by extrusion or molding for applications such as weatherstrip profile, seals, window gaskets and other soft touch articles. Attributes: Globalene TPV is a fully vulcanized Thermoplastic Elastomers containing EPDM and PP. It is designed for applications requiring long term sealing performance even at elevated temperatures. Suitable for injection molding, profile extrusion or re-compounding for plastics modification. Conventional thermoplastic processing equipment can be used. Applications: Globalene TPV has quality sealing property, good chemical and weathering resistance and electrical property that is suitable to replace main stream TPV, thermoset EPDM rubber, Styrene based TPEs, flexible PVC and other TPEs. It is an excellent choice for applications requiring flexibility in the following markets: automotive parts, appliance, business machines, construction, consumer products, and electronics.&& |
| Product Description | |
|---|---|
| Supplier | Lee Chang Yung |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good Electrical Properties,Good Hardness,Good Compression Set,High Heat Resistance,Baking,Ozone resistance,Solvent resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds, injection molding | 51 | ISO 868 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 23.0 | MPa | ISO 37 |
| 100% strain, 23 ℃ | 13.0 | MPa | ISO 37 |
| Tensile strain | |||
| Fracture, 23 ℃ | 600 | % | ISO 37 |
| tear strength | |||
| 23℃ | 110 | kN/m | ISO 34-1 |
| Compression deformation | |||
| 70℃，22 hr | 58 | % | |
| 125℃，70 hr | 83 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -30.0 | ℃ | ISO 812 |
| Melting temperature | 160 | ℃ | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ozone resistance | |||
| 500 hr，100 pphm O3 conc. | Excellent | ASTM D1149 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 180 to 190 | °C | |
| Barrel middle temperature | 200 to 220 | °C | |
| Barrel front temperature | 200 to 220 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Processing (melt) temperature | 200 to 220 | °C | |
| Mold temperature | 30 to 55 | °C | |
| Injection pressure | 4.80 to 6.90 | MPa | |
| Hold pressure | 2.10 to 4.10 | MPa | |
| Back pressure | 0.0689 to 1.03 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Vent depth | 0.025 | mm | |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 180 | °C | |
| Barrel 2 zone temperature | 190 | °C | |
| Barrel 3 zone temperature | 200 | °C | |
| Barrel 4 zone temperature | 210 | °C | |
| Barrel 5 zone temperature | 210 | °C | |
| Melt temperature | 180 to 220 | °C | |
| Nozzle temperature | 210 to 220 | °C | |
| Traction roller | 20 to 50 | °C | |
| Extruder screw length to diameter ratio L / D | >24.0:1.0 | ||
| Extruder screw compression ratio | 3.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |