Gordon Composites™ GC-67-UB

About
A continuous unidirectional “E” fiberglass/epoxy bar material that provides high strength and stiffness at all thickness ranges. GC-67-UB is manufactured with a proprietary pulforming process in which all glass fibers are pretensioned and aligned during the impregnation and curing process.&&

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.88	g/cm³	ASTM D1505

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
—	40000	MPa
—	10300	MPa
tensile strength
—	951	MPa
—	41.4	MPa
Tensile strain
fracture	2.3	%	ASTM D3039
Bending modulus	37900	MPa	ASTM D790
bending strength	1050	MPa	ASTM D790
Compression modulus
—	11700	MPa
—	40700	MPa
compressive strength
—	827	MPa
—	152	MPa
shear modulus
—	2900	MPa
—	4140	MPa
shear strength
—	61.4	MPa	ASTM D5397
—	32.4	MPa	ASTM D5379
Poisson’s ratio	0.30		ASTM D3410

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	121	℃	ASTM D3418

Notes
1. Width: .400″ to 8.75″ Thickness: .130″ to .550″ Length: 6″ to 264″
2. Typical properties: these are not to be construed as specifications.
3. 90 degree orientation
4. 0 degree orientation
5. Strength Values developed from ASTM D790 are dependent on thickness. As thickness increased flex strength decreased. The test data above is based on a test thickness of .060″
6. Inter-laminar, 2,3 direction
7. In-plane, 1,2 direction
8. nu12 (0/90), valid both tensile and compression
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.