| About |
|---|
| A light weight laminate composed of continuous unidirectional carbon fiber in an epoxy matrix, providing high strength and stiffness. GC-70-UCL is manufactured with a proprietary pulforming process in which all carbon fibers are pretensioned and aligned during impregnation and curing. This process assures the efficient utilization of the superior mechanical properties of the carbon fibers.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | 热固性复合材料 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ASTM D1505 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 152000 | MPa | |
| — | 9650 | MPa | |
| tensile strength | |||
| — | 2960 | MPa | |
| — | 48.3 | MPa | |
| Tensile strain | |||
| fracture | 1.9 | % | ASTM D3039 |
| Bending modulus | 137000 | MPa | ASTM D790 |
| bending strength | 2090 | MPa | ASTM D790 |
| Compression modulus | |||
| — | 11000 | MPa | |
| — | 134000 | MPa | |
| compressive strength | |||
| — | 1100 | MPa | |
| — | 165 | MPa | |
| Poisson’s ratio | 0.31 | ASTM D3039 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 116 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Available in roll form with lengths up to 250 ft. |
| 2. Width: 1.50″ to 8.75″ Thickness: .020″ to .045″ Length: 6″ to 120″ |
| 3. Typical properties: these are not to be construed as specifications. |
| 4. 90 degree orientation |
| 5. 0 degree orientation |
| 6. Strength Values developed from ASTM D790 are dependent on thickness. As thickness increased flex strength decreased. The test data above is based on a test thickness of .060″ |
| 7. nu12 (0/90) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |