| GPPC ABS D-1000S是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 GPPC ABS D-1000S的主要特性有: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Grand |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,5VA |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.7 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 55 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 3.2mm | 220 | J/m | ASTM D256 |
| 6.4mm | 180 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 81.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | |||
| 3.18 mm | 43.1 | MPa | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 2400 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 71.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Processing (melt) temperature | 180 to 210 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |