| About |
|---|
| Gravi-Tech™ GT6000-5015 LD Black 70 is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Europe. Applications of Gravi-Tech™ GT6000-5015 LD Black 70 include appliances, automotive, consumer goods and industrial applications. Characteristics include: RoHS Compliant Heat Stabilizer&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low density |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | ISO 527 |
| tensile strength | |||
| yield | 80.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 12 | kJ/m² | ISO 180/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 235 to 245 | °C | |
| Barrel front temperature | 240 to 250 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Mold temperature | 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |