| About |
|---|
| Grilamid® 1SBVX-55H nat是一种聚酰胺 1010（尼龙 1010）材料,含有的填充物为55% 玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Grilamid® 1SBVX-55H nat的主要特性有: 阻燃/额定火焰 冲击改性 环保/绿色 良好的抗紫外线能力 耐冲击 典型应用领域包括: 电气/电子应用 汽车行业 电气用具 工程/工业配件 工具 |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA 1010 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Renewable resources,Good liquidity,Good stripping performance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | |
| Shrinkage rate | |||
| TD | 0.30 | % | |
| MD | 0.10 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.7 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.90 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 15 | kJ/m² | |
| 23℃ | 20 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 85 | kJ/m² | |
| 23℃ | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 185 | ℃ | |
| 8.0 MPa, unannealed | 150 | ℃ | |
| Continuous use temperature | |||
| — | 100 | ℃ | |
| — | 150 | ℃ | |
| Melting temperature | 200 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.0E-5 | 1/℃ | |
| TD | 8.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | 1.0E+12 | ohms·cm | |
| Dielectric strength | 36 | kV/mm | |
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level (0.8 mm) | HB |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Type | PA1010+X, MH, 16-160 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 230 | MPa | |
| Tensile modulus | 17500 | MPa | |
| Tensile stress (fracture) | 210 | MPa | |
| Tensile strain | |||
| fracture | 2.5 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |